For railway and rolling mill bearings that bear large impact loads, the main failure forms when used after M quenching are: inner sleeve cracking during assembly, outer ring flange falling off and inner ring cracking during use, while isothermal quenched bearings have good impact toughness and surface compressive stress, no matter whether the inner sleeve cracking during assembly or the tendency of outer sleeve flange falling off and inner sleeve cracking during use is greatly reduced, And it can reduce the edge stress concentration of the roller. Therefore, the average service life and reliability after isothermal quenching are higher than those after M quenching. Provided by Longma bearing
0086-46461356843213
Luotuo Industrial Area, Zhenhai District, Ningbo City, Zhejiang Province, China
export@215987621646.com
Company Profile
Corporate Honors
Home
Product Center
Company Video
News Center
Contact Us
Case Center
Copyright @ 2020 Ningbo Sunplast Pipe Co., Ltd. All Rights Reserved.
Copyright 2018 a-life.cn All Rights Reserved
此站支持多端浏览
Business License Registration No.: 440301103091708 Copyright 2018 a-life.cn All Rights Reserved Headquarters address: 2604, 2605, Huichao science and technology building, Jinhai Road, Bao'an District, Shenzhen postcode: 518101